产品描述

XENOY PC/PBT/PET 1731A物性表

PBT+PC, Good Impact , Excellent physical property retention in automotive exteriors and OVAD.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
60
MPa
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
60
MPa
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
5.6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
108
%
ASTM D 638
Tensile Strain, brk, Type I, 10 mm/min
240
%
SABIC – Japan Method
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
2370
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
93
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
2120
MPa
ASTM D 790
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
60
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
57
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
5
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
104
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2370
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
92
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2210
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
814
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
176
J/m
ASTM D 256
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C, 6.4mm
160
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
58
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
59
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
16
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
65
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*4 sp=62mm
13
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
130
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
110
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
92
°C
ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed / 热变形温度,0.45 MPa, 6.4 mm, 未退火
120
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度,1.82 MPa, 6.4 mm, 未退火
105
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
8.32E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.35E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
8.32E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.35E-05
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
PASS
IEC 60695-10-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
130
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
131
°C
ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
116
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
98
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.22
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.65 – 0.73
%
SABIC Method
Melt Flow Rate / 熔流率, 250°C/5.0 kgf
9.6
g/10 min
ASTM D 1238
Density/密度
1.22
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
0.28
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
0.08
%
ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg
8
cm3/10 min
ISO 1133
Source GMD, last updated:10/16/2006
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
110
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
8
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
260 – 275
°C
Nozzle Temperature / 注嘴温度
255 – 270
°C
Front – Zone 3 Temperature / 前区3温度
255 – 275
°C
Middle – Zone 2 Temperature / 中区2温度
250 – 270
°C
Rear – Zone 1 Temperature / 后区1温度
245 – 265
°C
Mold Temperature / 模具温度
65 – 90
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
50 – 80
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
50 – 80
%
Vent Depth / 排气孔深度
0.013 – 0.02
mm
Source GMD, last updated:10/16/2006