产品描述

XENOY PC/PBT/PET 1402B物性表

1402B是一款可吹塑, 未增强PC/聚酯合金化聚合物。
特点:
极高的熔体粘度/强度
优异的低温抗冲击性
TYPICAL PROPERTIES (1)
MECHAN ICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
48
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
68
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
1990
MPa
ASTM D 790
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
694
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
534
J/m
ASTM D 256
Modified Gardner, 23°C
44
J
ASTM D 3029
THERMAL
Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度,1.82 MPa, 6.4 mm, 未退火
96
°C
ASTM D 648
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.19
ASTM D 792
Specific Volume/比容
0.84
cm3/g
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.9 – 1.1
%
SABIC Method
Mold Shrinkage on Tensile Bar, xflow (2)
0.9 – 1.1
%
SABIC Method
Source GMD, last updated:01/05/2000
Processing
Parameter
Extrusion Blow Molding
Value Unit
Drying Temperature / 干燥温度
95 – 100
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
24
hrs
Maximum Moisture Content / 最大含湿量
0.01 – 0.02
%
Minimum Moisture Content / 最小含湿量
0.02
%
Melt Temperature / 熔体温度(Parison)
240 – 250
°C
Barrel – Zone 1 Temperature / 第1气缸区温度
235 – 245
°C
Barrel – Zone 2 Temperature / 第2气缸区温度
235 – 245
°C
Barrel – Zone 3 Temperature / 第3气缸区温度
235 – 245
°C
Barrel – Zone 4 Temperature / 第4气缸区温度
235 – 245
°C
Adapter – Zone 5 Temperature / 接套-区域5 温度
235 – 245
°C
Head – Zone 6 – Top Temperature / 机头-区域6-上部温度
235 – 245
°C
Head – Zone 7 – Bottom Temperature / 机头-区域7-下部温度
235 – 245
°C
Mold Temperature / 模具温度
65 – 90
°C
Die Temperature / 模具温度
240 – 250
°C