产品描述

Xenoy PC/PBT/PET 1103物性表

相关颜色色号:1103-BK1066

AUTOMOTIVE. Unreinforced, impact modified PBT+PC alloy. Excellent low temperature impact and chemical resistance. Range gray, black colors.
Property/特性
TYPICAL PROPERTIES (1)
MECHANICAL/机械性能
Value/值 Unit/单位 Standard/标准
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
51
MPa
ASTM D 638
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
50
MPa
ASTM D 638
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
150
%
ASTM D 638
Tensile Modulus / 拉伸模量, 50 mm/min
1890
MPa
ASTM D 638
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
77
MPa
ASTM D 790
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
1930
MPa
ASTM D 790
IMPACT/冲击性能
Value/值 Unit/单位 Standard/标准
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
747
J/m
ASTM D 256
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
61
J
ASTM D 3763
THERMAL/热性能
Value/值 Unit/单位 Standard/标准
Vicat Softening Temp, Rate / 维卡软化温度,等级 B/50
125
°C
ASTM D 1525
HDT(热变形温度), 0.45 MPa, 3.2 mm, unannealed (未退火)
104
°C
ASTM D 648
HDT(热变形温度), 1.82 MPa, 3.2mm, unannealed (未退火)
87
°C
ASTM D 648
CTE(线形膨胀系数), -40°C to 40°C, flow(流动)
1.71E-04
1/°C
ASTM E 831
CTE(线形膨胀系数), -40°C to 40°C, xflow(横向)
2.E-04
1/°C
ASTM E 831
PHYSICAL/物理性能
Value/值 Unit/单位 Standard/标准
Specific Gravity / 比重
1.2
ASTM D 792
Mold Shrinkage / 收缩率, flow(流动), 3.2 mm
0.8 – 1
%
SABIC Method
Melt Flow Rate / 熔流率,, 250°C/5.0 kgf
13
g/10 min
ASTM D 1238
Source GMD, last updated:02/12/1999
Processing/加工方法
Parameter
Injection Molding/注塑参数
Value/值 Unit/单位
Drying Temperature / 干燥温度
110
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
8
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
255 – 275
°C
Nozzle Temperature / 注嘴温度
250 – 265
°C
Front – Zone 3 Temperature / 前区3温度
250 – 270
°C
Middle – Zone 2 Temperature / 中区2温度
245 – 265
°C
Rear – Zone 1 Temperature / 后区1温度
240 – 260
°C
Mold Temperature / 模具温度
40 – 90
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 80
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
50 – 80
%
Vent Depth / 排气孔深度
0.013 – 0.02
mm
Source GMD, last updated:02/12/1999