产品描述

ULTEM PEI 2200物性表

20% 玻纤增强,良好的刚度与尺寸稳定性。优异的可加工性。
相关颜色色号:2200-YW9119、2200-1000、2200-7301

20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. NSF 51 listing, WRAS certification in recognized colors.
Property/特性
TYPICAL PROPERTIES (1)
MECHANICAL/机械性能
Value/值 Unit/单位 Standard/标准
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 5 mm/min
131
MPa
ASTM D 638
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 5 mm/min
4
%
ASTM D 638
Tensile Modulus / 拉伸模量, 5 mm/min
6890
MPa
ASTM D 638
Flexural Stress, brk / 弯曲强度,断裂, 2.6 mm/min, 100 mm span
227
MPa
ASTM D 790
Flexural Modulus / 挠曲模量, 2.6 mm/min, 100 mm span
6890
MPa
ASTM D 790
Hardness,Rockwell / 洛氏硬度 M
114
ASTM D 785
IMPACT/冲击性能
Value/值 Unit/单位 Standard/标准
Izod Impact, unnotched / 无缺口悬臂梁冲击, 23°C
480
J/m
ASTM D 4812
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
64
J/m
ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm
464
J/m
ASTM D 256
THERMAL/热性能
Value/值 Unit/单位 Standard/标准
Vicat Softening Temp, Rate / 维卡软化温度,等级 B/50
220
°C
ASTM D 1525
HDT(热变形温度), 0.45 MPa, 6.4 mm, unannealed (未退火)
210
°C
ASTM D 648
HDT(热变形温度), 1.82 MPa, 6.4 mm, unannealed (未退火)
210
°C
ASTM D 648
CTE(线形膨胀系数), -20°C to 150°C, flow(流动)
2.52E-05
1/°C
ASTM E 831
Relative Temp Index, Elec / 相对热指数, 电性能
170
°C
UL 746B
Relative Temp Index, Mech w/impact / 相对热指数,机械冲击性能
170
°C
UL 746B
Relative Temp Index, Mech w/o impact / 相对热指数,非机械冲击性能
170
°C
UL 746B
PHYSICAL/物理性能
Value/值 Unit/单位 Standard/标准
Specific Gravity / 比重
1.42
ASTM D 792
Water Absorption / 吸水率, 24 hours
0.19
%
ASTM D 570
Water Absorption,equilibrium / 吸水率,平衡, 23C
1.1
%
ASTM D 570
Mold Shrinkage / 收缩率, flow(流动), 3.2 mm
0.3 – 0.5
%
SABIC Method
Melt Flow Rate / 熔流率,, 337°C/6.6 kgf
6
g/10 min
ASTM D 1238
ELECTRICAL/电气性能
Value/值 Unit/单位 Standard/标准
Volume Resistivity / 体积电阻率
7.E+16
Ohm-cm
ASTM D 257
Dielectric Strength, in oil / 耐电强度,在油中, 1.6 mm
26.3
kV/mm
ASTM D 149
Relative Permittivity / 相对介电常数, 1 kHz
3.5
ASTM D 150
Dissipation Factor / 耗散因素, 1 kHz
0.0015
ASTM D 150
Dissipation Factor / 耗散因素, 2450 MHz
0.0049
ASTM D 150
Arc Resistance, Tungsten / 耐电弧性 {PLC}
6
PLC Code
ASTM D 495
Hot Wire Ignition / 热丝引燃 {PLC)
1
PLC Code
UL 746A
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
2
PLC Code
UL 746A
High Ampere Arc Ign, surface / 高电流电弧引燃,表面 {PLC}
4
PLC Code
UL 746A
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
4
PLC Code
UL 746A
FLAME CHARACTERISTICS/火焰特性
Value/值 Unit/单位 Standard/标准
UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)
0.4
mm
UL 94
UL Recognized, 94-5VA Rating (3)
1.9
mm
UL 94
CSA (See File for complete listing)
LS88480
File No.
CSA LISTED
Oxygen Index / 极限氧指数 (LOI)
50
%
ASTM D 2863
NBS Smoke Density / 密度, Flaming, Ds 4 min
1.3
ASTM E 662
Source GMD, last updated:01/13/2000
Processing/加工方法
Parameter
Injection Molding/注塑参数
Value/值 Unit/单位
Drying Temperature / 干燥温度
150
°C
Drying Time / 干燥时间
4 – 6
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
24
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
350 – 400
°C
Nozzle Temperature / 注嘴温度
345 – 400
°C
Front – Zone 3 Temperature / 前区3温度
345 – 400
°C
Middle – Zone 2 Temperature / 中区2温度
340 – 400
°C
Rear – Zone 1 Temperature / 后区1温度
330 – 400
°C
Mold Temperature / 模具温度
135 – 165
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 70
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
40 – 60
%
Vent Depth / 排气孔深度
0.025 – 0.076
mm
Source GMD, last updated:01/13/2000