产品描述

NORYL PPO FXN2090H物性表

Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR additives to deliver UL94 V-0 performance at 1.5 mm. Noryl FXN2090H resin is currently available in custom black colors and may be an excellent material candidate for consumer electronics applications requiring high gloss aesthetics, scratch resistance and FR performance.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
66
MPa
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
55
MPa
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
3.7
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
7
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
2680
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
99
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
2510
MPa
ASTM D 790
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
66
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
58
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
3.6
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
6.3
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2640
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
105
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2660
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
100
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
45
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
17
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
5
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
3
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
5
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
109
°C
ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
84
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
7.5E+01
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.3E+01
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
7.5E+01
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.3E+01
1/°C
ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C
pass
IEC 60695-10-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
107
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
109
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
87
°C
ISO 75/Af
Relative Temp Index, Elec / 相对热指数, 电性能
65
°C
UL 746B
Relative Temp Index, Mech w/impact / 相对热指数,机械冲击性能
65
°C
UL 746B
Relative Temp Index, Mech w/o impact / 相对热指数,非机械冲击性能
65
°C
UL 746B
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.12
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.5 – 0.7
%
SABIC Method
Melt Flow Rate / 熔流率, 260°C/2.16 kgf
9
g/10 min
ASTM D 1238
Density/密度
1.12
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
0.18
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
0.06
%
ISO 62
Melt Volume Rate, MVR at 280°C/2.16 kg
25
cm3/10 min
ISO 1133
OPTICAL
Value Unit Standard
Gloss, untextured, 60 degrees / 光泽度,无纹理,60度
97
ASTM D 523
ELECTRICAL
Value Unit Standard
Hot Wire Ignition {PLC) / 热丝引燃 {PLC)
0
PLC Code
UL 746A
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
1.5
mm
UL 94
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
1
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm / 热灯丝点火温度, 1.0 mm
725
°C
IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm
725
°C
IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm / 热灯丝点火温度, 3.0 mm
750
°C
IEC 60695-2-13
Source GMD, last updated:04/30/2007
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
60 – 70
°C
Drying Time / 干燥时间
2 – 4
hrs
Maximum Moisture Content / 最大含湿量
0.02
%
Melt Temperature / 熔体温度
240 – 270
°C
Nozzle Temperature / 注嘴温度
240 – 260
°C
Front – Zone 3 Temperature / 前区3温度
240 – 260
°C
Middle – Zone 2 Temperature / 中区2温度
240 – 250
°C
Rear – Zone 1 Temperature / 后区1温度
240
°C
Mold Temperature / 模具温度
70 – 90
°C
Back Pressure / 背压
0.3 – 0.7
MPa
Screw Speed / 螺杆速度
40 – 70
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
30 – 70
%
Vent Depth / 排气孔深度
0.038 – 0.051
mm
Source GMD, last updated:04/30/2007