产品描述

NORYL PPO EXNL0222物性表

Experimental Noryl* EXNL0222 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for light weight parts. Noryl EXNL0222 is available in custom colors and may be an excellent material candidate for applications requiring strong flame, smoke and toxicity performance.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
64
MPa
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
53
MPa
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
4.6
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
20
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
2220
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
100
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
2390
MPa
ASTM D 790
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
64
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
58
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
4.7
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
8.3
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2440
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
100
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2360
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
300
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
52
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
18
kJ/m2
ISO 180/1A
THERMAL
Value Unit Standard
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
122
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
6.7E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
6.7E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
6.7E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
6.7E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
146
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
124
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.11
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.5 – 0.8
%
SABIC Method
Melt Flow Rate / 熔流率, 300°C/2.16 kgf
4.8
g/10 min
ASTM D 1238
Density/密度
1.11
g/cm3
ISO 1183
Melt Volume Rate, MVR at 300°C/2.16 kg
4
cm3/10 min
ISO 1133
Source GMD, last updated:11/14/2006
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
95 – 105
°C
Drying Time / 干燥时间
2 – 4
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
12
hrs
Melt Temperature / 熔体温度
280 – 305
°C
Nozzle Temperature / 注嘴温度
295 – 305
°C
Front – Zone 3 Temperature / 前区3温度
295 – 305
°C
Middle – Zone 2 Temperature / 中区2温度
290 – 300
°C
Rear – Zone 1 Temperature / 后区1温度
280 – 295
°C
Mold Temperature / 模具温度
65 – 100
°C
Screw Speed / 螺杆速度
40 – 80
rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比
30 – 70
%
Parameter
Sheet Extrusion
Value Unit
Drying Temperature / 干燥温度
95 – 105
°C
Drying Time / 干燥时间
2 – 4
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
12
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
220 – 260
°C
Barrel – Zone 1 Temperature / 第1气缸区温度
220 – 260
°C
Barrel – Zone 2 Temperature / 第2气缸区温度
220 – 260
°C
Barrel – Zone 3 Temperature / 第3气缸区温度
220 – 260
°C
Barrel – Zone 4 Temperature / 第4气缸区温度
220 – 260
°C
Adapter Temperature / 连接器温度
220 – 260
°C
Die Temperature / 模具温度
220 – 260
°C
Roll Stack Temp – Top
90 – 150
°C
Roll Stack Temp – Middle
90 – 150
°C
Roll Stack Temp – Bottom
90 – 150
°C
Parameter
Profile Extrusion
Value Unit
Drying Temperature / 干燥温度
95 – 105
°C
Drying Time / 干燥时间
2 – 4
hrs
Drying Time (Cumulative) / 干燥时间(累积的)
12
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
220 – 260
°C
Barrel – Zone 1 Temperature / 第1气缸区温度
220 – 260
°C
Barrel – Zone 2 Temperature / 第2气缸区温度
220 – 260
°C
Barrel – Zone 3 Temperature / 第3气缸区温度
220 – 260
°C
Barrel – Zone 4 Temperature / 第4气缸区温度
220 – 260
°C
Hopper Temperature / 料筒温度
80 – 120
°C
Adapter Temperature / 连接器温度
220 – 260
°C
Die Temperature / 模具温度
220 – 260
°C
Calibrator Temperature
30 – 60
°C
Water Bath Temperature
30 – 50
°C
Source GMD, l ast updated:11/14/2006