产品描述

NORYL PPO EXNL0141物性表

Noryl* EXNL0141 is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this resin uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating. Noryl EXNL0141 is available in colors and may be an excellent choice for a wide variety of applications including hand held devises, housings and displays.

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min
64
MPa
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min
53
MPa
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min
4.8
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min
30
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
2300
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
97
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
2400
MPa
ASTM D 790
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
60
mg/1000cy
SABIC Method
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
63
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
52
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
4.6
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
30
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2350
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
92
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2300
MPa
ISO 178
Hardness, H358/30 / 球压硬度,H358/30
105
MPa
ISO 2039-1
Hardness, Rockwell R / 硬度, 洛氏 R
119
ISO 2039-2
IMPACT
Value Unit Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
120
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
70
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
41
J
ASTM D 3763
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
11
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
7
kJ/m2
ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,23°C,C80*10*4 sp=62mm
14
kJ/m2
ISO 179/1eA
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度,-30°C,C80*10*4 sp=62mm
7
kJ/m2
ISO 179/1eA
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
137
°C
ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
130
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
116
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
8.2E+01
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.5E+01
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
8.2E+01
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
8.5E+01
1/°C
ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
Passes
IEC 60695-10-2
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
135
°C
ISO 306
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
138
°C
ISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
130
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
115
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.08
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.5 – 0.7
%
SABIC Method
Melt Flow Rate / 熔流率, 280°C/5.0 kgf
7
g/10 min
ASTM D 1238
Density/密度
1.08
g/cm3
ISO 1183
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
0.23
%
ISO 62
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
0.06
%
ISO 62
Melt Volume Rate, MVR at 280°C/5.0 kg
7
cm3/10 min
ISO 1133
OPTICAL
Value Unit Standard
Gloss, untextured, 60 degrees / 光泽度,无纹理,60度
20
ASTM D 523
FLAME CHARACTERISTICS
Value Unit Standard
UL Recognized, 94V-1 Flame Class Rating (3) / UL认可,94V-1 阻燃等级(3)
1.5
mm
UL 94
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
3.2
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 3.0 mm / 热灯丝点火温度, 3.0 mm
700
°C
IEC 60695-2-13
Source GMD, last updated:01/05/2006
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
80 – 100
°C
Drying Time / 干燥时间
2 – 3
hrs
Melt Temperature / 熔体温度
280 – 300
°C
Nozzle Temperature / 注嘴温度
260 – 280
°C
Front – Zone 3 Temperature / 前区3温度
280 – 300
°C
Middle – Zone 2 Temperature / 中区2温度
260 – 280
°C
Rear – Zone 1 Temperature / 后区1温度
240 – 260
°C
Hopper Temperature / 料筒温度
60 – 80
°C
Mold Temperature / 模具温度
60 – 100
°C
Source GMD, last updated :01/05/2006