产品描述

NORYL PPO EXNL0065物性表

EXNL0065 is a 10% glass fiber reinforced, heat stabilized, low odor and low emission NORYL(R) grade for interior automotive applications, especially instrument panels

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min
68
MPa
ISO 527
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
68
MPa
ISO 527
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min
2.3
%
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
2.5
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
4400
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
110
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
3800
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, unnotched 80*10*4 +23°C
23
kJ/m2
ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
22
kJ/m2
ISO 180/1U
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
24
kJ/m2
ISO 179/1eU
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
127
°C
ISO 306
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度,1.8 MPa, 未退火, 100 mm 跨距
115
°C
ISO 75/Ae
PHYSICAL
Value Unit Standard
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率,流动
0.3 – 0.5
%
SABIC Method
Density/密度
1.13
g/cm3
ISO 1183
Melt Volume Rate, MVR at 300°C/2.16 kg
18
cm3/10 min
ISO 1133
Source GMD, last updated:12/04/2003
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
100 – 110
°C
Drying Time / 干燥时间
2 – 3
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
280 – 300
°C
Nozzle Temperature / 注嘴温度
270 – 290
°C
Front – Zone 3 Temperature / 前区3温度
280 – 300
°C
Middle – Zone 2 Temperature / 中区2温度
270 – 290
°C
Rear – Zone 1 Temperature / 后区1温度
260 – 280
°C
Hopper Temperature / 料筒温度
60 – 80
°C
Mold Temperature / 模具温度
80 – 100
°C
Source GMD, last updated:12/04/2003