产品描述

NORYL PPO 8370HS物性表

8370HS is a compounded PPO* concentrate with polystyrene

TYPICAL PROPERTIES (1)
MECHANICAL机械性能 Value Unit Standard
Tensile Stress, yield 50 mm/min / 抗张程度,屈服, 50 mm/min
73
MPa
ISO 527
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
61
MPa
ISO 527
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
5.1
%
ISO 527
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
6
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
2500
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
108
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
2600
MPa
ISO 178
IMPACT
Value Unit Standard
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
10
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
6
kJ/m2
ISO 180/1A
THERMAL
Value Unit Standard
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
167
°C
ISO 306
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
134
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Density/密度
1.06
g/cm3
ISO 1183
Melt Volume Rate, MVR at 280°C/10.0 kg
7
cm3/10 min
ISO 1133
Source GMD, last updated:02/28/2006
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
100 – 110
°C
Drying Time / 干燥时间
2 – 3
hrs
Maximum Moisture Content / 最大含湿量
0.07
%
Melt Temperature / 熔体温度
300 – 320
°C
Nozzle Temperature / 注嘴温度
280 – 300
°C
Front – Zone 3 Temperature / 前区3温度
300 – 320
°C
Middle – Zone 2 Temperature / 中区2温度
280 – 300
°C
Rear – Zone 1 Temperature / 后区1温度
260 – 280
°C
Hopper Temperature / 料筒温度
80 – 100
°C
Mold Temperature / 模具温度
100 – 120
°C
Source GMD, la st updated:02/28/2006