产品描述

LNP VERTON MV006BS物性表

LNP VERTON MV006BS是一种聚丙烯产品,含有的填充物为30%长玻璃纤维,可以通过注射成型进行加工。
典型应用领域为:工程/工业配件。
特性包括:
化学耦合
热稳定剂
TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
104
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
104
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
2.3
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
2.3
%
ASTM D 638
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min
6930
MPa
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距
162
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
5840
MPa
ASTM D 790
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min
96
MPa
ISO 527
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
87
MPa
ISO 527
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min
2.2
%
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
2.2
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
6330
MPa
ISO 527
Flexural Stress
145
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
0
MPa
ISO 178
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
770
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
214
J/m
ASTM D 256
Multiaxial Impact
6
J
ISO 6603
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
12
J
ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C
53
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
20
kJ/m2
ISO 180/1A
THERMAL
Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
163
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
155
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
7.6E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
7.6E-05
1/°C
ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
162
°C
ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 热变形温度,1.8 MPa, 未退火,80*10*4, 64.0 mm 跨距
155
°C
ISO 75/Af
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.09
ASTM D 792
Density/密度
1.09
g/cm3
ASTM D 792
Moisture Absorption, 50% RH, 24 hrs
0.03
%
ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)
0.3 – 0.6
%
ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)
0.5 – 0.8
%
ASTM D 955
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
0.02
%
ISO 62
Source GMD, last updated:2009/12/31
Processing
Parameter
Injection Molding
Value Unit
Drying Temperature / 干燥温度
80
°C
Drying Time / 干燥时间
4
hrs
Melt Temperature / 熔体温度
220 – 250
°C
Front – Zone 3 Temperature / 前区3温度
250 – 260
°C
Middle – Zone 2 Temperature / 中区2温度
245 – 255
°C
Rear – Zone 1 Temperature / 后区1温度
230 – 245
°C
Mold Temperature / 模具温度
40 – 65
°C
Back Pressure / 背压
0.2 – 0.3
MPa
Screw Speed / 螺杆速度
30 – 60
rpm
Sour ce GMD, last updated:2009/12/31