CYCOLOY PC/ABS C4210HF物性表

PC+ABS Blend with 10% Glass Reinforce. High flow, High heat resistance., Excellent balance strength/rigidity. Good IMPACT/appearance.
相关色号:C4210HF-76701

TYPICAL PROPERTIES (1)
MECHANICAL机械性能
Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min
85
MPa
ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min
85
MPa
ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min
3
%
ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min
3
%
ASTM D 638
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min
4900
MPa
ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span
140
MPa
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距
4300
MPa
ASTM D 790
Tensile Stress, yield 5 mm/min / 抗张程度,屈服, 5 mm/min
90
MPa
ISO 527
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min
90
MPa
ISO 527
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min
3.2
%
ISO 527
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
4700
MPa
ISO 527
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
125
MPa
ISO 178
Flexural Stress, break, 2 mm/min
135
MPa
ISO 178
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
4250
MPa
ISO 178
Hardness, H358/30 / 球压硬度,H358/30
116
MPa
ISO 2039-1
Hardness, Rockwell R / 硬度, 洛氏 R
121
ISO 2039-2
IMPACT
Value Unit Standard
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C
480
J/m
ASTM D 4812
Izod IMPACT, unnotched, -30°C
480
J/m
ASTM D 4812
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
75
J/m
ASTM D 256
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C
60
J/m
ASTM D 256
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量,23°C
15
J
ASTM D 3763
Instrumented IMPACT Total Energy, -30°C / 装有测量仪表的落镖冲击Total Energy,-30°C
8
J
ASTM D 3763
Izod IMPACT, unnotched 80*10*4 +23°C
30
kJ/m2
ISO 180/1U
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度,80*10*4 +23°C
8
kJ/m2
ISO 180/1A
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度,80*10*4 -30°C
6
kJ/m2
ISO 180/1A
THERMAL
Value Unit Standard
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火
134
°C
ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火
126
°C
ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度,1.82 MPa, 6.4 mm, 未退火
128
°C
ASTM D 648
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动
4.E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向
7.5E-05
1/°C
ASTM E 831
Thermal Conductivity / 导热系数
0.2
W/m-°C
ISO 8302
PHYSICAL
Value Unit Standard
Specific Gravity/比重
1.22
ASTM D 792
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量,流动,3.2 mm
0.3 – 0.5
%
SABIC Method
Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量,横向,3.2 mm
0.3 – 0.5
%
SABIC Method
Melt Flow Rate / 熔流率, 260°C/5.0 kgf
37
g/10 min
ASTM D 1238
Source GMD, last updated:03/18 /2005